MG Chemicals 9510-3.6L One-Part Epoxy Potting Compound
4.3 (20 items)
Limited Time SaleUntil the end
09
16
04
$875.49 cheaper than the new price!!
Free shipping for purchases over $99 ( Details )
Free cash-on-delivery fees for purchases over $99
Free cash-on-delivery fees for purchases over $99
See all stores
Please note that the sales price and tax displayed may differ between online and in-store. Also, the product may be out of stock in-store.
New $1,750.99
Product details
| Management number | 201657353 | Release Date | 2025/10/04 | List Price | $875.50 | Model Number | 201657353 | ||
|---|---|---|---|---|---|---|---|---|---|
| Category | |||||||||
General Information
Manufacturer
MG Chemical
Part Number
9510-3.6L
Product Type
Epoxy Potting Compound
Return Policy
NON-CANCELLABLE / NON-REFUNDABLE
California Residents
Specifications
Color
Black
Material
Epoxy Resin
Size
3.6 L (per unit)
Weight
14.97 kg
33.00 lb
Miscellaneous
What's Included
(3) Cans
Features
Resistivity 2.6 x 10-13 Ω·cm
Breakdown Voltage: 36 700 V
Dielectric Strength: 540 V/mil
Hardness: 84 D
Tensile Strength: 20 N/mm2
Compressive Strength: 90 N/mm2
Lap Shear
(stainless steel): 9.2 N/mm2
(aluminum): 5.8 N/mm2
Glass Transition Temperature (Tg): 70 ˚C
CTE Prior Tg: 74 ppm/˚C
CTE After Tg: 217 ppm/˚C
Thermal Conductivity @ 25 ˚C: 0.3 W/(m·K)
Service Temperature Range: -65–150 ˚C
Intermittent Temperature: 295 ˚C
Cure Times:
3 h @ 80 ˚C
1 h @ 90 ˚C
30 min @ 120 ˚C
Breakdown Voltage: 36 700 V
Dielectric Strength: 540 V/mil
Hardness: 84 D
Tensile Strength: 20 N/mm2
Compressive Strength: 90 N/mm2
Lap Shear
(stainless steel): 9.2 N/mm2
(aluminum): 5.8 N/mm2
Glass Transition Temperature (Tg): 70 ˚C
CTE Prior Tg: 74 ppm/˚C
CTE After Tg: 217 ppm/˚C
Thermal Conductivity @ 25 ˚C: 0.3 W/(m·K)
Service Temperature Range: -65–150 ˚C
Intermittent Temperature: 295 ˚C
Cure Times:
3 h @ 80 ˚C
1 h @ 90 ˚C
30 min @ 120 ˚C